Eight places and reasons why quartz stone is easy to crack

 Eight places and reasons why quartz stone is easy to crack

When purchasing quartz stone countertops, many consumers are blinded by the price of quartz stone. They think that the quality of quartz stone countertops can be much worse. In fact, the truth of high-end and low-end inferior quality is very different, so consumers are buying When making quartz stone countertops, it is recommended that you still choose the products produced by high-end and large-scale quartz stone manufacturers, otherwise the following quality problems are prone to occur:

⑴. Cracking at the seam of the countertop: When the main installation worker is splicing, the seam is not aligned, the top of the bell is small and the bottom is large, the glue is not evenly spread, and more importantly, the F clamp is not used to fix the glue after the glue is applied, or Adding curing agent to the glue or accelerating the excessive amount of the economy will make the joints more brittle and crack when subjected to slight impact during use;

⑵ Cracks at the corners: the wall is too tight and no shrinkage joints are left, the height between the two cabinets is uneven or not leveled, the front corner is opened at a right angle, and the internal stress is concentrated.

⑶. Cracking around the above counter basin: there is no gap between the above counter basin and the basin hole, the basin hole is not polished and smooth, the four corners of the basin hole are not rounded or there are serrated marks, and the table surface shrinks unevenly and cracks due to external impact or temperature changes;

⑷ Cracking around the furnace hole: there is no gap between the gas stove and the furnace hole, the furnace hole is not polished and smooth, the four corners of the basin hole are not rounded or there are jagged marks, and the table surface is not uniformly shrunk due to external impact or temperature changes and cracks;

⑸. Cracks in the skirts of the above counter basins and stove holes: the load of the cabinets, basin cabinets or stove cabinets is placed flat, when the above counter basins, the skirts of the stove holes are subjected to gravity (people stepping, stepping, etc.) The skirt before the hole is cracked;

⑹. Cracking of the rear water barrier: the cabinet is uneven or the backing board is not leveled;

⑺. Cracking of the connecting surface of the rear water retaining edge: the glue is not firmly bonded;

⑻. Cracks in the center of the countertop: high temperature, external impact, uneven cabinets or backing plates, internal damage to the board, etc.; therefore, the main factor causing countertop cracks is the poor quality control of the countertop during processing.